SrO

Notes

-Together with CaO, BaO, and MgO it is considered one the Alkaline Earth group of oxides.

-Does not break down till 1090C (cone 02) so it is not useful as a glaze flux below this temperature. SrO must thus be employed in frit form below 1090C to be effective.

-It has an expansion akin to CaO and a similar decomposition behavior.

-Strontium compounds have not been widely used because of their more limited availability, although the value of this oxide has long been known.

-It is very useful at lower temperatures (i.e. cone 1) for high gloss, craze resistant glazes which develop a good interface with the clay body. The interface development is thought to occur due to the mixed-oxide effect (bodies do not normally contain SrO).

-Strontium is important because of its non-hazardous, non-poisonous nature. With it, glazes of all temperatures can be made free of lead and barium (in spite of its different expansion, it can be a viable substitute for small proportions of lead).

-Even though it has a very high melting temperature, SrO is an effective flux above 650C when interacting with other oxides (provided it is added in fritted form).

-Like CaO and ZnO, it forms a crystal matte surface on cooling if dominant in the RO group. Conversely, a diversity of fluxing oxides associated with SrO will reduce crystallization.

-SrO has been used with success as a substitute for lead oxide in glazes using smaller amounts. Glossy glazes melting as low as cone 01 without any zinc are possible (long soaking periods may be necessary). Like lead, strontium develops vivid colors.

-Small additions of SrO can improve the surface of viscous high fire zirconium glazes.

-If BaO is replaced in whole or in part with SrO, glazes can develop better interface and have a lower expansion. However, they may also be less elastic than those formed by Ba and this could lead to fit problems where body and glaze are not closely compatible. SrO has a different color response to copper and cobalt; it has a lower expansion, and is a little more powerful at fluxing.

-The lower temperature decomposition of SrCO3 potentially produces an earlier reaction of SrO giving the melt more time to clear of bubbles and pits.

Properties
Surface Modifier	Like calcia and baria, it will produce a fine crystalline mesh to give attractive satin matte surfaces.